Polimeri Europa Clearflex® H&T LGH 138 Octene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex® H&T
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® H&T LGH 138 Octene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex H&T LGH 138 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, slip agent, antiblocking and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T LGH 138 show excellent optical properties, a wide sealing window, both hot tack and hot seal, together with a low sealing initiation temperature (S.I.T.) and outstanding impact, puncture and Elmendorf tear resistance.Main Applications: Clearflex H&T LGH 138, for its overall characteristics, is the right choice for packaging film applications requiring superior mechanical and optical properties. The excellent sealability behavior together with low gel content makes it ideal for lamination film production.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.917 g/cc
0.917 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ISO 527-3
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ISO 527-3
Film Elongation at Break, MD 450 %
450 %
ISO 527-3
Film Elongation at Break, TD 700 %
700 %
ISO 527-3
Coefficient of Friction, Dynamic 0.11
0.11
ISO 8295
Elmendorf Tear Strength, MD 11.209 g/micron
284.71 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 20.38 g/micron
517.7 g/mil
ISO 6383-2
Dart Drop Test 350 g
0.772 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ISO 527-3
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
1% Secant Modulus, MD 160 MPa
23200 psi
ISO 527-3
1% Secant Modulus, TD 170 MPa
24700 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 117 °C
243 °F
Internal method
Vicat Softening Point 102 °C

@Load 1.00 kg
216 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 11 %
11 %
ISO 14782
Gloss 55 %
55 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified