Polimeri Europa Clearflex® FG 336 Hexene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® FG 336 Hexene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex FG 336 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidant, slip agent, antiblocking agent and processing aid, suitable for blown film extrusion.Films obtained from Clearflex FG 336 show high rigidity together with optimum Elmendorf tear and impact resistance.Main Applications: Clearflex FG 336 is recommended for shipping sacks, where the perfect balance between additives (in terms of slip and antiblocking) and mechanical performance leads to the manufacture of a tough and easily peelable film. Moreover, for its sealing characteristics, together with low temperature mechanical resistance, Clearflex FG 336 is suggested for the production of freezer bags, either in coextrusion or in blend with LDPE.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.926 g/cc
0.926 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.0 MPa
1740 psi
ISO 527-3
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527-3
Film Elongation at Break, MD 550 %
550 %
ISO 527-3
Film Elongation at Break, TD 740 %
740 %
ISO 527-3
Coefficient of Friction, Dynamic 0.11
0.11
ISO 8295
Elmendorf Tear Strength, MD 8.3558 g/micron
212.24 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 25.475 g/micron
647.07 g/mil
ISO 6383-2
Dart Drop Test 120 g
0.265 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 45.0 MPa
6530 psi
ISO 527-3
Film Tensile Strength at Break, TD 36.0 MPa
5220 psi
ISO 527-3
1% Secant Modulus, MD 180 MPa
26100 psi
ISO 527-3
1% Secant Modulus, TD 200 MPa
29000 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
Internal method
Vicat Softening Point 110 °C

@Load 1.00 kg
230 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 13 %
13 %
ISO 14782
Gloss 54 %
54 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified