Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex CL 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 106 are characterized by high clarity, optimum elongation at break and optimum impact and tear resistance.Main Applications: Clearflex CL 106 is recommended for the production of low cling cast film with high optical properties and good mechanical resistance. It is ideal for the production of power stretch film characterized by a medium pre-stretch.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.920 g/cc
0.920 g/cc
ISO 1183
Thickness 8.00 - 50.0 microns
0.315 - 1.97 mil
Recommended
Melt Flow 3.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ISO 527-3
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ISO 527-3
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 800 %
800 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 12.228 g/micron
310.59 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 23.437 g/micron
595.30 g/mil
ISO 6383-2
Dart Drop Test 120 g
0.265 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 38.0 MPa
5510 psi
ISO 527-3
Film Tensile Strength at Break, TD 29.0 MPa
4210 psi
ISO 527-3
1% Secant Modulus, MD 180 MPa
26100 psi
ISO 527-3
1% Secant Modulus, TD 190 MPa
27600 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
Internal method
Vicat Softening Point 97.0 °C

@Load 1.00 kg
207 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 2.5 %
2.5 %
ISO 14782
Gloss 90 %
90 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified