Polikim KESTLUB® Polyamide 6 + Lubricant

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Polikim Polimer ve Kimya Sanay
Trade Name KESTLUB®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polikim KESTLUB® Polyamide 6 + Lubricant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kestlub® is a special type of cast polyamide ideal for bearings. It is produced by adding lubricants to cast polyamide through special processes. It performs extremely well in bearing applications as it is self-lubricated. Lubricants are homogenously dispersed making them inseperable out of the material. Lubricant additivess do not leak out even in toughest operating conditions. Machining does not alter this qualilty. Lubrication keeps the coefficient of friction very low during operation and thus prevents heating up, extending component operation life. Kestlub® should be used in applications where dimensional stability and weatherability of Kestamid® are questionable. As lubricant additives fill up pores, humidity and water absorption are reduced; sustaining dimensional stability. In high pressures and bearing applications, solid lubricant does not leak out.Information provided by Polikim Polimer.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Water Absorption at Saturation 5.0 %
5.0 %
ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 84
84
ISO 868
Tensile Strength, Ultimate 78.5 MPa
11400 psi
ISO 527
Elongation at Break >= 20 %
>= 20 %
ISO 527
Tensile Modulus 4.00 GPa
580 ksi
ISO 527
Compressive Strength 93.2 MPa
13500 psi
ISO 604
Compressive Modulus 2.60 GPa
377 ksi
ISO 604
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Charpy Impact Unnotched NB
NB
ISO 179
Coefficient of Friction 0.080
0.080
K Factor (Wear Factor) 0.020
0.020
[mg/km]
K (wear) Factor 25.0 x 10-8 mm³/N-M
12.4 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 110 °C
230 °F
continuous
170 °C
338 °F
short term
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ISO 60093
Surface Resistance >= 1.00e+13 ohm
>= 1.00e+13 ohm
ISO 60093
Dielectric Constant 3.7
3.7
ISO 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
ISO 50243