Poco Graphite ZXF-5Q Industrial Grade Graphite

Category Carbon , Graphite
Manufacturer Poco Graphite
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Poco Graphite ZXF-5Q Industrial Grade Graphite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SSH hardness is 86.General Poco Specialty Graphite Information: Poco's high strength, fine-grained, isotropic graphites offer maximum design flexibility. Easily machined. High strength and small particle size allow fabrication of complex components containing tight tolerances. Post synthesis treatments available include purification or impregnation with resins, oxidation inhibitors, or metals. Surface treatments offer improved wear characteristics and particle reduction.Some applications of Poco specialty graphites include anode plates for wet cells, fuel cell plates for solid polymer cells, air bearings, hot gas valves, high temperature bearings, bushings, and seals, hot press dies and rams, furnace furniture/fixturing, rocket engine nozzles, molten metal casting components, vacuum furnace heating elements, space vehicle nose cones, mirrors and optical structures, and satellite heat shields.
Physical Properties Metric English Comments
Apparent Bulk Density 1.78 g/cc
0.0643 lb/in³
Open Porosity 80 %
80 %
Porosity 20 %
20 %
Particle Size 1.0 µm
1.0 µm
Pore Size 0.300 microns
0.0118 mil
Mechanical Properties Metric English Comments
Hardness, Shore D 86
86
Tensile Strength, Yield 79.0 MPa
11500 psi
Elongation at Yield 0.78 %
0.78 %
Modulus of Elasticity 14.5 GPa
2100 ksi
Flexural Strength 112 MPa
16200 psi
Compressive Strength 175 MPa
25400 psi
Thermal Properties Metric English Comments
CTE, linear 8.10 µm/m-°C
4.50 µin/in-°F
Thermal Conductivity 70.0 W/m-K
486 BTU-in/hr-ft²-°F
Electrical Properties Metric English Comments
Electrical Resistivity 0.00195 ohm-cm
0.00195 ohm-cm