Plenco 504 Black (INJ) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound  (discontinued **)<

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Heat Resistant Grade, Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 504 Black (INJ) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound  (discontinued **)<.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding compounds. Since it also has good electrical properties, it has found use in a wide variety of wiring device applications.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ASTM D792
Apparent Bulk Density 0.600 g/cc
0.0217 lb/in³
ASTM D1895
Water Absorption 0.20 %
0.20 %
ASTM D570
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
Injection; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 52.0 MPa
7540 psi
ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ASTM D790
Compressive Yield Strength 193 MPa
28000 psi
ASTM D695
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 166 °C
331 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.47 mm
302 °F

@Thickness 0.0579 in
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 5.0

@Frequency 1e+6 Hz
5.0

@Frequency 1e+6 Hz
ASTM D150
7.0

@Frequency 60 Hz
7.0

@Frequency 60 Hz
ASTM D150
Dielectric Strength 15.7 kV/mm
399 kV/in
ASTM D149
Dissipation Factor 0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
ASTM D150
0.090

@Frequency 60 Hz
0.090

@Frequency 60 Hz
ASTM D150
Comparative Tracking Index 180 V
180 V
UL 746