Plenco 1586 Polyester, Pellet, Transfer Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC
Manufacturer Plenco (Plastics Engineering Company)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 1586 Polyester, Pellet, Transfer Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PLENCO 01586 is a glass and mineral reinforced pelletized polyester molding compound offering excellent heat resistance and mechanical strength properties. This product is typically used for injection molded electrical appliance components. UL recognized under component file E40654. 01586 is available in white.Information supplied by Plenco.
Physical Properties Metric English Comments
Bulk Density 0.950 g/cc
0.0343 lb/in³
ASTM D1895
Density 1.92 g/cc
0.0694 lb/in³
ASTM D792
Water Absorption 0.068 %
0.068 %
ASTM D570
Linear Mold Shrinkage 0.00192 cm/cm
0.00192 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 51
51
ASTM D785
Tensile Strength, Ultimate 76.0 MPa
11000 psi
ASTM D638
Elongation at Break 1.32 %
1.32 %
ASTM D638
Tensile Modulus 10.8 GPa
1570 ksi
ASTM D638
Flexural Strength 119 MPa
17300 psi
ASTM D790
Flexural Modulus 10.2 GPa
1480 ksi
ASTM D790
Compressive Strength 157 MPa
22800 psi
ASTM D695
Izod Impact, Notched 0.770 J/cm
1.44 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.720 J/cm²
3.43 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 211 °C
412 °F
Heat Resistance; ASTM D570D
Deflection Temperature at 1.8 MPa (264 psi) 267 °C
513 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.00 mm
V-0

@Thickness 0.0394 in
Oxygen Index 36 %
36 %
ASTM D2863
Shrinkage 0.0114 %
0.0114 %
72 hr, 120ºC; ASTM D1299
Electrical Properties Metric English Comments
Volume Resistivity 1.20e+15 ohm-cm
1.20e+15 ohm-cm
ASTM D247
Dielectric Constant 4.2
4.2
ASTM D150
Dielectric Strength 11.3 kV/mm
287 kV/in
Step by Step; ASTM D149
12.4 kV/mm
315 kV/in
Short Time; ASTM D149
Dielectric Breakdown 23000 V

@Temperature 121 °C,
Time 3600 sec
23000 V

@Temperature 250 °F,
Time 1.00 hour
ASTM D149
Dissipation Factor 0.0129
0.0129
ASTM D150
Arc Resistance 187 sec
187 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
ASTM D3638