Plastics Group Polifil® T-10 10% Talc-Reinforced Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer The Plastics Group of America
Trade Name Polifil®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastics Group Polifil® T-10 10% Talc-Reinforced Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colorability, low shrinkage and yield maximum stiffness combined with characteristic impact.Applications: Automotive (underhood) applicationsMajor appliancesElectrical goodsHousewaresStandard processing techniques are applicable. Information provided by The Plastics Group.
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
ASTM D792
Filler Content 10 %
10 %
ASTM D2584
Linear Mold Shrinkage 0.012 cm/cm

@Thickness 1.59 mm
0.012 in/in

@Thickness 0.0625 in
ASTM D955
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
230/2.16; May be specified; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 97
97
ASTM D785
Tensile Strength at Break 28.3 MPa
4100 psi
ASTM D638
Flexural Modulus 1.86 GPa
270 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.400 J/cm
0.750 ft-lb/in
At 73°F; ASTM D256
Izod Impact, Unnotched 3.58 J/cm
6.70 ft-lb/in
At 73°F; ASTM D256
Gardner Impact 0.565 J
0.417 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
245 °F
ASTM D648