PlastiComp Complet® LGF20 - PA6 Nylon 6, 20% Long Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer PlastiComp
Trade Name Complēt®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PlastiComp Complet® LGF20 - PA6 Nylon 6, 20% Long Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 20% long glass reinforcementInformation provided by PlastiComp, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D-792
Filler Content 20 %
20 %
Long Glass Fiber
Mechanical Properties Metric English Comments
Tensile Strength 128 MPa
18600 psi
ASTM D-638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D-638
Tensile Modulus 8.276 GPa
1200 ksi
ASTM D-638
Flexural Strength 203 MPa
29400 psi
ASTM D-790
Flexural Modulus 7.586 GPa
1100 ksi
ASTM D-790
Izod Impact, Notched 1.87 J/cm
3.50 ft-lb/in
ASTM D-256
Izod Impact, Unnotched 10.68 J/cm
20.01 ft-lb/in
ASTM D-4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 188 °C
370 °F
ASTM D-648
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 277 °C
500 - 530 °F
Middle Barrel Temperature 266 - 282 °C
510 - 540 °F
Front Barrel Temperature 271 - 288 °C
520 - 550 °F
Nozzle Temperature 271 - 288 °C
520 - 550 °F
Melt Temperature 271 - 288 °C
520 - 550 °F
Mold Temperature 93.3 °C
200 °F
Injection Velocity 50.8 - 76.2 mm/sec
2.00 - 3.00 in/sec
Drying Temperature 85.0 °C

@Time 14400 sec
185 °F

@Time 4.00 hour
Moisture Content <= 0.18 %
<= 0.18 %
Back Pressure 0.172 - 0.345 MPa
25.0 - 50.0 psi
Cushion 0.635 cm
0.250 in
Screw Speed 30 - 50 rpm
30 - 50 rpm
Descriptive Properties Value Comments
Injection Pressure Medium to maximum