PlastiComp Complet® LCF40 - PA66 Nylon 66, 40% Long Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Carbon Fiber Filled
Manufacturer PlastiComp
Trade Name Complēt®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PlastiComp Complet® LCF40 - PA66 Nylon 66, 40% Long Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 40% carbon fiber reinforcementInformation provided by PlastiComp, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D-792
Filler Content 40 %
40 %
Carbon Fiber
Mechanical Properties Metric English Comments
Tensile Strength 276 MPa
40000 psi
ASTM D-638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D-638
Tensile Modulus 29.655 GPa
4301.1 ksi
ASTM D-638
Flexural Strength 414 MPa
60000 psi
ASTM D-790
Flexural Modulus 21.448 GPa
3110.8 ksi
ASTM D-790
Izod Impact, Notched 2.94 J/cm
5.51 ft-lb/in
ASTM D-256
Izod Impact, Unnotched 11.21 J/cm
21.00 ft-lb/in
ASTM D-4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 246 °C
475 °F
ASTM D-648
Processing Properties Metric English Comments
Rear Barrel Temperature 282 - 299 °C
540 - 570 °F
Middle Barrel Temperature 288 - 304 °C
550 - 580 °F
Front Barrel Temperature 293 - 310 °C
560 - 590 °F
Nozzle Temperature 288 - 304 °C
550 - 580 °F
Melt Temperature 293 - 310 °C
560 - 590 °F
Mold Temperature 93.3 °C
200 °F
Injection Velocity 50.8 - 76.2 mm/sec
2.00 - 3.00 in/sec
Drying Temperature 85.0 °C

@Time 14400 sec
185 °F

@Time 4.00 hour
Moisture Content <= 0.18 %
<= 0.18 %
Back Pressure 0.172 - 0.345 MPa
25.0 - 50.0 psi
Cushion 0.635 cm
0.250 in
Screw Speed 30 - 50 rpm
30 - 50 rpm
Descriptive Properties Value Comments
Injection Pressure Medium to maximum