PlastiComp Complet® LCF30 - PP Homopolymer Polypropylene, 30% Long Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Carbon Fiber Filled
Manufacturer PlastiComp
Trade Name Complēt®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PlastiComp Complet® LCF30 - PP Homopolymer Polypropylene, 30% Long Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 30% carbon fiber reinforcementInformation provided by PlastiComp, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D-792
Filler Content 30 %
30 %
Carbon Fiber
Mechanical Properties Metric English Comments
Tensile Strength 117 MPa
17000 psi
ASTM D-638
Elongation at Break 1.0 %
1.0 %
ASTM D-638
Tensile Modulus 16.207 GPa
2350.6 ksi
ASTM D-638
Flexural Strength 186 MPa
27000 psi
ASTM D-790
Flexural Modulus 12.759 GPa
1850.5 ksi
ASTM D-790
Izod Impact, Notched 2.14 J/cm
4.01 ft-lb/in
ASTM D-256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D-4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
ASTM D-648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 210 °C
390 - 410 °F
Middle Barrel Temperature 204 - 216 °C
400 - 420 °F
Front Barrel Temperature 210 - 221 °C
410 - 430 °F
Nozzle Temperature 204 - 216 °C
400 - 420 °F
Melt Temperature 210 - 221 °C
410 - 430 °F
Mold Temperature 79.4 °C
175 °F
Injection Velocity 50.8 - 76.2 mm/sec
2.00 - 3.00 in/sec
Back Pressure 0.172 - 0.345 MPa
25.0 - 50.0 psi
Cushion 0.635 cm
0.250 in
Screw Speed 30 - 50 rpm
30 - 50 rpm
Descriptive Properties Value Comments
Injection Pressure Medium to maximum