- Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant
Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVASTER® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVASTER® B GF 20 FRK 3 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesPBT with the content of 20% chemically coupled glass fiber and flame retardant based on red phosphorus. Anisotropy of shrinkage enables injection moulding of round, cylindrical or other hole products. Application in engineering, electrical and automotive industry. High mechanical properties also in conditioned state. Delivered in natural and black color.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0049 cm/cm | 0.0049 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0088 cm/cm | 0.0088 in/in | STN 64 0808 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | STN EN ISO 527-2 |
| Flexural Strength | 175 MPa | 25400 psi | STN EN ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| 5.50 J/cm² @Temperature -20.0 °C |
26.2 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 200 - 220 °C | 392 - 428 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | STN EN ISO 75/A |
| Vicat Softening Point | 210 °C | 410 °F | B; STN EN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 960 °C | 1760 °F | STN IEC 60695-2-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | STN IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | STN IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | STN IEC 60243 |
| Comparative Tracking Index | 200 V | 200 V | STN 34 6468 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.050 % | 0.050 % | STN EN ISO 960 |
| Injection Pressure | 60.0 - 100 MPa | 8700 - 14500 psi |