Plastcom SLOVAMID 6 GF 50 Polyamide 6, 50% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 GF 50 Polyamide 6, 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6 for injection moulding, chemically strengthened with 50% of glass fiber, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling screws of blowers, electromotors, carrying parts in the automotive industry. Delivered in natural mode and in the full RAL color scale. Lightly impacted.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
STN 64 0808
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
STN EN ISO 527-2
Elongation at Break 2.0 %
2.0 %
STN EN ISO 527-2
Tensile Modulus 14.5 GPa
2100 ksi
STN EN ISO 527-2
Flexural Strength 290 MPa
42100 psi
STN EN ISO 178
Flexural Modulus 12.5 GPa
1810 ksi
STN EN ISO 178
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -20.0 °C
40.4 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 1.50 J/cm²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
STN EN ISO 75/A
Vicat Softening Point 210 °C
410 °F
B; STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
STN IEC 60695-2-10
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+13 ohm-cm
5.00e+13 ohm-cm
STN IEC 60093
Surface Resistance 8.00e+13 ohm
8.00e+13 ohm
STN IEC 60093
Dielectric Strength 40.0 kV/mm
1020 kV/in
STN IEC 60243
Comparative Tracking Index 575 V
575 V
STN 34 6468
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 90.0 - 100 °C
194 - 212 °F
Drying Temperature 90.0 °C
194 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi