Plastcom SLOVAMID® 6 GF 25 FRC 4 PA6 reinforced with glass fiber, flame retarded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID® 6 GF 25 FRC 4 PA6 reinforced with glass fiber, flame retarded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 for injection molding, reinforced with 25 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability according to UL 94 3 at 1,6mm, glow wire at 960°C. Application for the electrical industry: protectors, coil forms, covers, terminals. Delivered in natural color or in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
STN EN ISO 1183-1
Filler Content 25 %
25 %
Linear Mold Shrinkage 0.0075 cm/cm
0.0075 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0112 cm/cm
0.0112 in/in
STN EN ISO 294-4
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
STN EN ISO 527-2
Elongation at Break 2.0 %
2.0 %
STN EN ISO 527-2
Tensile Modulus 12.0 GPa
1740 ksi
STN EN ISO 527-2
Flexural Strength 205 MPa
29700 psi
STN EN ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
STN EN ISO 178
Charpy Impact Unnotched 4.40 J/cm²

@Temperature -20.0 °C
20.9 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
4.80 J/cm²

@Temperature 23.0 °C
22.8 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.750 J/cm²

@Temperature 23.0 °C
3.57 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
0.750 J/cm²

@Temperature -20.0 °C
3.57 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 210 °C
410 °F
STN EN ISO 306
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
STN EN 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
STN 34 6460
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
STN 34 6460
Dielectric Strength 60.0 kV/mm
1520 kV/in
STN EN 60243-2
Comparative Tracking Index 600 V
600 V
STN EN 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi