Plastcom SLOVAMID® 6 GF 20 FRA 5 PA6 reinforced with glass fiber, flame retarded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVAMID® 6 GF 20 FRA 5 PA6 reinforced with glass fiber, flame retarded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6 for injection molding, reinforced with 20% glass fiber, flame retarded with halogen flame retardant. Main features: flammability in accordance with UL 94 5 at 1.6 mm, glow wire at 960°C. Application for the electrical industry: protectors, coil forms, covers, terminals. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | STN EN ISO 294-4 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | STN EN ISO 527-2 |
| Elongation at Break | 3.0 % | 3.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | STN EN ISO 527-2 |
| Flexural Strength | 145 MPa | 21000 psi | STN EN ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -20.0 °C |
23.8 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 230 °C | 446 °F | STN EN ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
STN EN 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | STN 34 6460 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | STN 34 6460 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | STN EN 60243-2 |
| Comparative Tracking Index | 300 V | 300 V | STN EN 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 % | 0.15 % | STN EN ISO 3344 |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |