Plastcom SLOVALEN PH 72 T 40 PP, 40% mineral filling

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PH 72 T 40 PP, 40% mineral filling.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, thermo stable, chemically modified talc. General application in all industry branches - covers of car chassis, fenders, motors etc. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
Linear Mold Shrinkage 0.0144 cm/cm
0.0144 in/in
Linear Mold Shrinkage, Transverse 0.0165 cm/cm
0.0165 in/in
Melt Flow 10 g/10 min

@Load 0.325 kg,
Temperature 270 °C
10 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
Elongation at Break 5.5 %
5.5 %
Tensile Modulus 3.60 GPa
522 ksi
Flexural Strength 47.0 MPa
6820 psi
Flexural Modulus 3.70 GPa
537 ksi
Charpy Impact Unnotched 2.30 J/cm²

@Temperature -20.0 °C
10.9 ft-lb/in²

@Temperature -4.00 °F
2.80 J/cm²

@Temperature 23.0 °C
13.3 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.140 J/cm²

@Temperature -20.0 °C
0.666 ft-lb/in²

@Temperature -4.00 °F
0.270 J/cm²

@Temperature 23.0 °C
1.28 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Vicat Softening Point 160 °C
320 °F
B
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi