- Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber
Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 40% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0082 cm/cm | 0.0082 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm | 0.0077 in/in | STN 64 0808 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | STN EN ISO 527-2 |
| Flexural Strength | 140 MPa | 20300 psi | STN EN ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 4.70 J/cm² @Temperature -20.0 °C |
22.4 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 4.80 J/cm² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | STN EN ISO 75/A |
| Vicat Softening Point | 165 °C | 329 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |