Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified homopolymer PP for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal use up to 120°C. Decreased shrinkage. General application in all industry branches - packing material, garden flower-pots, toys, furniture industry, dowels, clamps, hinge, office chairs, hangers, covers of car chassis, fenders, motors etc. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.005 g/cc
0.03631 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0183 cm/cm
0.0183 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0145 cm/cm
0.0145 in/in
STN 64 0808
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
STN EN ISO 527-2
Elongation at Break 10 %
10 %
STN EN ISO 527-2
Tensile Modulus 2.00 GPa
290 ksi
STN EN ISO 527-2
Flexural Strength 45.0 MPa
6530 psi
STN EN ISO 178
Flexural Modulus 2.00 GPa
290 ksi
STN EN ISO 178
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
9.52 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.400 J/cm²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
STN EN ISO 75/A
Vicat Softening Point 155 °C
311 °F
B; STN EN ISO 306
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 50.0 °C
104 - 122 °F
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi