Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Glass Reinforced, Impact Modified
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified copolymer PP for injection moulding, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Linear Mold Shrinkage 0.0168 cm/cm
0.0168 in/in
Linear Mold Shrinkage, Transverse 0.0175 cm/cm
0.0175 in/in
Melt Flow 15 g/10 min

@Load 0.325 kg,
Temperature 270 °C
15 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa
2900 psi
Elongation at Break 3.0 %
3.0 %
Tensile Modulus 1.50 GPa
218 ksi
Flexural Strength 30.0 MPa
4350 psi
Flexural Modulus 1.50 GPa
218 ksi
Charpy Impact Unnotched 1.00 J/cm²

@Temperature -20.0 °C
4.76 ft-lb/in²

@Temperature -4.00 °F
1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.100 J/cm²

@Temperature -20.0 °C
0.476 ft-lb/in²

@Temperature -4.00 °F
0.200 J/cm²

@Temperature 23.0 °C
0.952 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 145 °C
293 °F
Deflection Temperature at 1.8 MPa (264 psi) 68.0 °C
154 °F
Vicat Softening Point 150 °C
302 °F
B
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C
1760 °F
at 3 mm
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi