Plastcom SLOVALEN EH 96 FRD 2 PP, flame retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN EH 96 FRD 2 PP, flame retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesDetermined for environment, where contact with water is possible, because the electric properties do not change by conditioning. Application - terminals, coil forms, guides in washing machines, tea-pots, dish-washers. Delivered in natural mode and in the full RAL colour scale. Modified homopolymer PP, retarded type with halogen flame retardant. Fulfills basic electric properties: flammability in accordance with UL 94 V2 and 850°C glow wire.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
Linear Mold Shrinkage 0.0238 cm/cm
0.0238 in/in
Linear Mold Shrinkage, Transverse 0.0217 cm/cm
0.0217 in/in
Melt Flow 15 g/10 min

@Load 0.325 kg,
Temperature 270 °C
15 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 18.0 MPa
2610 psi
Elongation at Break 33 %
33 %
Tensile Modulus 1.20 GPa
174 ksi
Flexural Strength 21.0 MPa
3050 psi
Flexural Modulus 0.900 GPa
131 ksi
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -20.0 °C
21.4 ft-lb/in²

@Temperature -4.00 °F
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Charpy Impact, Notched 0.600 J/cm²

@Temperature -20.0 °C
2.86 ft-lb/in²

@Temperature -4.00 °F
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 130 °C
266 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 100 °C
212 °F
B
Flammability, UL94 V-2
V-2
Glow Wire Test 850 °C
1560 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
Dielectric Strength 28.0 kV/mm
711 kV/in
Comparative Tracking Index 500 V
500 V
Processing Properties Metric English Comments
Melt Temperature 170 - 190 °C
338 - 374 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Injection Pressure 50.0 - 80.0 MPa
7250 - 11600 psi