Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Plastcom PLASTAMID® 66 GF 20 PA66 reinforced with glass fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name PLASTAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom PLASTAMID® 66 GF 20 PA66 reinforced with glass fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA66 reinforced with 20 % glass fiber, used in the automotive, engineering and electrical industry. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
STN EN ISO 1183-1
Linear Mold Shrinkage 0.0079 cm/cm
0.0079 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0019 cm/cm
0.0019 in/in
STN EN ISO 294-4
Melt Flow 3.0 g/10 min

@Load 0.325 kg,
Temperature 275 °C
3.0 g/10 min

@Load 0.716 lb,
Temperature 527 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 5.50 GPa
798 ksi
STN EN ISO 527-2
Flexural Strength 185 MPa
26800 psi
STN EN ISO 178
Flexural Modulus 4.50 GPa
653 ksi
STN EN ISO 178
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
4.00 J/cm²

@Temperature -20.0 °C
19.0 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
3.81 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 250 °C
482 °F
STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C

@Thickness 3.00 mm
1200 °F

@Thickness 0.118 in
STN EN 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi