Plastcom PLASTAMID® 66 GF 15 T 15 TS PA66 reinforced with glass fibers and mineral filler, heat stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled
Manufacturer	Plastcom spol. s r.o.
Trade Name	PLASTAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom PLASTAMID® 66 GF 15 T 15 TS PA66 reinforced with glass fibers and mineral filler, heat stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Black PA66 for injection molding, reinforced with 15% glass fiber and 15% mineral filler, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, gears, covers of electric tools, automobile mirror housings, cooling screws of blowers, electric motors, bearing parts in the automotive industry.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	STN EN ISO 1183-1
Filler Content	15 %	15 %	Glass Fiber
	15 %	15 %	Mineral
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	STN EN ISO 294-4
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	STN EN ISO 294-4
Melt Flow	2.0 g/10 min @Load 0.325 kg, Temperature 275 °C	2.0 g/10 min @Load 0.716 lb, Temperature 527 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	95.0 MPa	13800 psi	STN EN ISO 527-2
Elongation at Break	3.5 %	3.5 %	STN EN ISO 527-2
Tensile Modulus	4.70 GPa	682 ksi	STN EN ISO 527-2
Flexural Strength	175 MPa	25400 psi	STN EN ISO 178
Flexural Modulus	3.90 GPa	566 ksi	STN EN ISO 178
Charpy Impact Unnotched	4.50 J/cm² @Temperature -20.0 °C	21.4 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	5.00 J/cm² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	0.350 J/cm² @Temperature -20.0 °C	1.67 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	0.400 J/cm² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	250 °C	482 °F	STN EN ISO 306
Flammability, UL94	HB	HB
Glow Wire Test	650 °C @Thickness 3.00 mm	1200 °F @Thickness 0.118 in	STN EN 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	STN 34 6460
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	STN 34 6460
Dielectric Strength	30.0 kV/mm	762 kV/in	STN EN 60243-2
Comparative Tracking Index	450 V	450 V	STN EN 60112

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.10 %	0.10 %	STN EN ISO 3344
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi

Descriptive Properties	Value	Comments
Color	Black