Plastcom PLASTAMID® 66 BT SD PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | PLASTAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom PLASTAMID® 66 BT SD PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Basic type PA66 for injection molding, modified for general use. PA66 contains TiO2 up to 0.5% wt. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, hobby tools, toys. Delivered in the natural color.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | STN EN ISO 1183-1 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | STN EN ISO 294-4 |
| Melt Flow | 12 g/10 min @Load 0.325 kg, Temperature 275 °C |
12 g/10 min @Load 0.716 lb, Temperature 527 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | STN EN ISO 527-2 |
| Elongation at Break | 1.5 % | 1.5 % | STN EN ISO 527-2 |
| Tensile Modulus | 3.20 GPa | 464 ksi | STN EN ISO 527-2 |
| Flexural Strength | 75.0 MPa | 10900 psi | STN EN ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| 4.50 J/cm² @Temperature -20.0 °C |
21.4 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 250 °C | 482 °F | STN EN ISO 306 |
| Flammability, UL94 | V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
|
| Glow Wire Test | 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
STN EN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.25 % | 0.25 % | STN EN ISO 3344 |
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |