Plastcom PLASTAMID® 6 GF 30 005 PA6 reinforced with glass fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Plastcom spol. s r.o.
Trade Name	PLASTAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom PLASTAMID® 6 GF 30 005 PA6 reinforced with glass fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6 for injection molding, reinforced with 30% glass fiber, used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, gears, covers of electric tools, automobile mirror housings, cooling screws of blowers, electromotors, bearing parts in the automotive industry. Delivered in black color. Cost effective solution in comparison with Slovamid line.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	STN EN ISO 1183-1
Filler Content	30 %	30 %
Linear Mold Shrinkage	0.011 cm/cm	0.011 in/in	STN EN ISO 294-4
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in	STN EN ISO 294-4
Melt Flow	5.0 g/10 min @Load 5.00 kg, Temperature 270 °C	5.0 g/10 min @Load 11.0 lb, Temperature 518 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	155 MPa	22500 psi	STN EN ISO 527-2
Elongation at Break	3.0 %	3.0 %	STN EN ISO 527-2
Tensile Modulus	8.65 GPa	1250 ksi	STN EN ISO 527-2
Flexural Strength	195 MPa	28300 psi	STN EN ISO 178
Flexural Modulus	6.85 GPa	994 ksi	STN EN ISO 178
Charpy Impact Unnotched	4.50 J/cm² @Temperature -20.0 °C	21.4 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	5.50 J/cm² @Temperature 23.0 °C	26.2 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	0.600 J/cm² @Temperature -20.0 °C	2.86 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	222 °C	432 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	215 °C	419 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	225 °C	437 °F	STN EN ISO 306
Flammability, UL94	HB	HB
Glow Wire Test	650 °C @Thickness 3.00 mm	1200 °F @Thickness 0.118 in	STN EN 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	STN 34 6460
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	STN 34 6460
Dielectric Strength	25.0 kV/mm	635 kV/in	STN EN 60243-2
Comparative Tracking Index	350 V	350 V	STN EN 60112

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 290 °C	500 - 554 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.15 %	0.15 %	STN EN ISO 3344
Injection Pressure	80.0 - 130 MPa	11600 - 18900 psi

Descriptive Properties	Value	Comments
Color	Black