Plastcom PLASTALEN® PH 52 T 20 003/1M Polypropylene reinforced with 20% mineral filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Plastcom spol. s r.o.
Trade Name PLASTALEN®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom PLASTALEN® PH 52 T 20 003/1M Polypropylene reinforced with 20% mineral filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
STN EN ISO 1183-1
Filler Content 20 %
20 %
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
STN EN ISO 294-4
Melt Flow 5.0 - 15 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 - 15 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
STN EN ISO 527-2
Elongation at Break 5.0 %
5.0 %
STN EN ISO 527-2
Tensile Modulus 2.00 GPa
290 ksi
STN EN ISO 527-2
Flexural Strength 35.0 MPa
5080 psi
STN EN ISO 178
Flexural Modulus 1.70 GPa
247 ksi
STN EN ISO 178
Charpy Impact Unnotched 1.30 J/cm²

@Temperature -20.0 °C
6.19 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
3.20 J/cm²

@Temperature 23.0 °C
15.2 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.130 J/cm²

@Temperature -20.0 °C
0.619 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.230 J/cm²

@Temperature 23.0 °C
1.09 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 115 °C
239 °F
STN EN ISO 306
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.10 %
0.10 %
STN EN ISO 3344
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi
Descriptive Properties Value Comments
Color Black