Plaskolite West Optix® CA - 2000 High Impact Acrylic Resin

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded
Manufacturer Plaskolite West, Inc.
Trade Name Optix®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plaskolite West Optix® CA - 2000 High Impact Acrylic Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists gamma ray radiation sterilization which also meet US Pharmacopoeia XXI class VI toxicity requirements, and FDA food additive regulation 21 CFR 177.1010 (acrylic and modified acrylic plastics, semi-rigid, and rigid).Information provided by Plaskolite West, Inc.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D-955
Melt Flow 2.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Tensile Strength 38.6 MPa
5600 psi
ASTM D-638
Elongation at Break 40 %
40 %
ASTM D-638
Modulus of Elasticity 1.86 GPa
270 ksi
ASTM D-638
Flexural Strength 66.2 MPa
9600 psi
ASTM D-790
Izod Impact, Notched 1.07 J/cm

@Thickness 6.35 mm
2.00 ft-lb/in

@Thickness 0.250 in
ASTM D-256
Gardner Impact 9.04 J

@Thickness 3.17 mm
6.67 ft-lb

@Thickness 0.125 in
Falling Weight; ASTM D-3029 GB
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C
33.3 µin/in-°F
ASTM D-696
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ASTM D-648
Vicat Softening Point 100 °C
212 °F
ASTM D-1525
Optical Properties Metric English Comments
Haze <= 3.0 %
<= 3.0 %
ASTM D-1003
Transmission, Visible 91 %
91 %
ASTM D-1003