- Phillips 66 COPYLENE® CH005 Polypropylene, Homopolymer, Extrusion, Strapping
Phillips 66 COPYLENE® CH005 Polypropylene, Homopolymer, Extrusion, Strapping
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Phillips 66 |
| Trade Name | COPYLENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Phillips 66 COPYLENE® CH005 Polypropylene, Homopolymer, Extrusion, Strapping.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
COPYLENE® CH005 is a fractional melt flow polypropylene homopolymer resin available in pellet form.Information provided by Phillips 66.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ASTM D792 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.2 MPa | 5100 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | ASTM D638 |
| Flexural Modulus | 1.62 GPa | 235 ksi | 0.05 in/min; 1% secant; Procedure A; ASTM D790 |
| Flexural Modulus, 1% Secant | 1620 MPa | 235000 psi | 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Extrusion | |
| Region | Mexico | |
| US & Canada |