Petroquimica Triunfo Trithene® TX 7010 LDPE - Medium Duty Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Petroquimica Triunfo
Trade Name Trithene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trithene® TX 7010 LDPE - Medium Duty Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trithene® TX 7010 resin is a low-density polyethylene (LDPE) with high molecular weight, excellent processability with very good mechanical properties. Besides these properties, the material is characterized by excellent draw-down and shrinkage properties. Contains no additives. This product complies with ASTM standard D1248-IA4 and the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1520 (c) 2.1, to contact with foodstuff.Applications: Thin and general purpose films. Thin shrink film. Coextrusion with PA (Nylon), EVA, PP.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.921 - 0.923 g/cc
0.0333 - 0.0333 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.80 - 1.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 - 1.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 12.5 MPa
1810 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 625 %
625 %
ASTM D882
Elongation at Break 500 %
500 %
ASTM D638
Secant Modulus, MD 0.100 GPa
14.5 ksi
5%; ASTM D882
Secant Modulus, TD 0.110 GPa
16.0 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.60
0.60
ASTM D1894
Elmendorf Tear Strength, MD 8.00 g/micron
203 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.40 g/micron
112 g/mil
ASTM D1922
Dart Drop Test 180 g
0.397 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 22.5 MPa
3260 psi
ASTM D882
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 91.0 °C
196 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 9.5 %
9.5 %
ASTM D1003
Gloss 52 %
52 %
45° - Gardner; ASTM D2457
85 %
85 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 155 - 165 °C
311 - 329 °F
Plasticizing Zone
165 - 175 °C
329 - 347 °F
Mixture Zone
Feed Temperature 150 - 160 °C
302 - 320 °F
Adapter Temperature 175 - 185 °C
347 - 365 °F
Blow-up Ratio (BUR) 3.0
3.0
Recommended