Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Petroquimica Triunfo
Trade Name Trithene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trithene TU 3001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical properties, good processability and bubble stability. These qualities ensure the production of very wide films with uniform thickness and excellent resistance to UV-radiation. The additive package warrants thermal and light stabilization for greenhouse mid-life films with very good resistance to the traditional soil disinfecting and crop protection chemicals normally applied in agriculture. This product complies with ASTM standard D1248-IA5.Applications: Films for covering of greenhouses and both large and small tunnels. Films for applications that require high mechanical strength and high resistance to aging from solar radiation (UV radiation exposure).Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.922 - 0.924 g/cc
0.0333 - 0.0334 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.12 - 0.16 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.12 - 0.16 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 18.0 MPa
2610 psi
ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
ASTM D638
Film Elongation at Break, MD 595 %
595 %
ASTM D882
Film Elongation at Break, TD 740 %
740 %
ASTM D882
Elongation at Break 595 %
595 %
ASTM D638
Secant Modulus, MD 0.0920 GPa
13.3 ksi
5%; ASTM D882
Secant Modulus, TD 0.0910 GPa
13.2 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.40
0.40
ASTM D1894
Elmendorf Tear Strength, MD 8.80 g/micron
224 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 14.4 g/micron
366 g/mil
ASTM D1922
Dart Drop Test 395 g
0.871 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 16 %
16 %
ASTM D1003
Gloss 62 %
62 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 195 °C
356 - 383 °F
Mixture Zone
Feed Temperature 170 - 185 °C
338 - 365 °F
Adapter Temperature 200 - 220 °C
392 - 428 °F
Blow-up Ratio (BUR) 3.0
3.0
Recommended
Descriptive Properties Value Comments
UV Stabilizer ppm 5750-6500
PTN-579-Q`