Petroquimica Triunfo Trithene® TN 7006 LDPE - Coextruded Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Petroquimica Triunfo
Trade Name	Trithene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Petroquimica Triunfo Trithene® TN 7006 LDPE - Coextruded Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Trithene® TS 7006 resin is a low-density polyethylene (LDPE) with high molecular weight and very good clarity. The unique combination of good processability, bubble stability, gloss, and strength meet all the requirements for barrier films coextrusion, even for very thin structures. The antioxidant package allows for very good thermal stability during processing. This product complies with ASTM standard D1248-IA4.Applications: High clarity films, coextruded with polyamide, EVOH, PVdC, etc. for food packaging, such as: cheese, meat, sausages, sliced ham, etc.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas

Physical Properties	Metric	English	Comments
Density	0.923 - 0.926 g/cc	0.0333 - 0.0335 lb/in³	ASTM D1505
Thickness	50.0 microns	1.97 mil
Melt Index of Compound	0.50 - 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.50 - 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	16.0 MPa	2320 psi	ASTM D638
Tensile Strength, Yield	12.0 MPa	1740 psi	ASTM D638
Film Elongation at Break, MD	350 %	350 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Elongation at Break	575 %	575 %	ASTM D638
Secant Modulus, MD	0.117 GPa	17.0 ksi	5%; ASTM D882
Secant Modulus, TD	0.125 GPa	18.1 ksi	5%; ASTM D882
Coefficient of Friction, Dynamic	0.55	0.55	ASTM D1894
Elmendorf Tear Strength, MD	7.40 g/micron	188 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	5.70 g/micron	145 g/mil	ASTM D1922
Dart Drop Test	160 g	0.353 lb	(method A); ASTM D1709
Film Tensile Strength at Break, MD	26.0 MPa	3770 psi	ASTM D882
Film Tensile Strength at Break, TD	23.0 MPa	3340 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	97.0 °C	207 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	8.5 %	8.5 %	ASTM D1003
Gloss	90 %	90 %	@ 60° Gardner; ASTM D2457

Processing Properties	Metric	English	Comments
Processing Temperature	155 - 165 °C	311 - 329 °F	Plasticizing Zone; Monoextrusion
	165 - 175 °C	329 - 347 °F	Mixture Zone; Monoextrusion
	170 - 180 °C	338 - 356 °F	Plasticizing Zone; Coextrusion with polyamide
	180 - 190 °C	356 - 374 °F	Mixture Zone; Coextrusion with polyamide
Feed Temperature	150 - 160 °C	302 - 320 °F	Mono-extrusion
	160 - 170 °C	320 - 338 °F	Co-extrusion with Polyamide
Adapter Temperature	175 - 185 °C	347 - 365 °F	Mono-extrusion
	220 - 230 °C	428 - 446 °F	Co-extrusion with Polyamide
Blow-up Ratio (BUR)	3.0	3.0	Recommended

Users viewing this material also viewed the following: