Petroquimica Triunfo Trithene® JX 7065 LDPE - Injection Molding and Master Batch

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Petroquimica Triunfo
Trade Name Trithene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trithene® JX 7065 LDPE - Injection Molding and Master Batch.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trithene® JX 7065 resin is a low-density polyethylene with a wide molecular weight distribution, developed to offer good impact resistance, excellent flexibility, and high resistance to stress cracking. This product presents good processability for a wide range of mold conditions. This product complies with ASTM standard D1248-IA3.Applications: Injection molding of toys and household utensils that need good Environmental Stress Cracking Resistance (ESCR). Production of Master Batch for dyeing and concentrate of additives such as slip agent, anti-block, anti-static, etc.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.916 - 0.920 g/cc
0.0331 - 0.0332 lb/in³
ASTM D1505
Viscosity 57 cP

@Shear Rate 3000 1/s,
Temperature 190 °C
57 cP

@Shear Rate 3000 1/s,
Temperature 374 °F
ASTM D3835
111 cP

@Shear Rate 1000 1/s,
Temperature 190 °C
111 cP

@Shear Rate 1000 1/s,
Temperature 374 °F
ASTM D3835
217000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
217000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
ASTM D3835
Melt Index of Compound 5.0 - 8.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 - 8.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 8.50 MPa
1230 psi
ASTM D638
Tensile Strength, Yield 9.50 MPa
1380 psi
ASTM D638
Elongation at Break 300 %
300 %
ASTM D638
Thermal Properties Metric English Comments
CTE, linear 230 µm/m-°C

@Temperature 20.0 °C
128 µin/in-°F

@Temperature 68.0 °F
dilatation; ASTM D696
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ASTM D177
Melting Point 110 °C
230 °F
ASTM D3418
Vicat Softening Point 83.0 °C
181 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 190 - 280 °C
374 - 536 °F
Injection Molding
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F