Petroquimica Triunfo Trilene® TS 5009 LLDPE-C4 and LDPE Blend

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , LLDPE
Manufacturer Petroquimica Triunfo
Trade Name Trilene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trilene® TS 5009 LLDPE-C4 and LDPE Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trilene TS 5009 product is a blend with a high ratio of linear low-density polyethylene (LLDPE) with low-density polyethylene (LDPE) with elevated processability, ensuring the production of films with uniform thickness and good visual appearance and weldability. The additive package gives it thermal stability, low blocking and adequate slip performance, which are indispensable to allow high productivity on the extrusion, printing, and finishing lines. The formulation of this product was developed for direct use with design extruders or adapted for the processing of LLDPE. The components that form the product Trilene TS 5009 complies with the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1520 (c) 2.1, to contact with foodstuff.Applications: Technical laminated films designed for packaging of various products such as coffee, crackers, etc. Technical films for automatic or semi-automatic packaging of solid products (grains, powdered, etc.), liquids (milk, yot, etc.), and frozen foods (poultry, beef cuts, seafood, ice, etc.).Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 845 %
845 %
ASTM D882
Film Elongation at Break, TD 940 %
940 %
ASTM D882
Secant Modulus, MD 0.108 GPa
15.7 ksi
5%; ASTM D882
Secant Modulus, TD 0.110 GPa
16.0 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.15
0.15
ASTM D1894
Elmendorf Tear Strength, MD 3.90 g/micron
99.1 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 16.9 g/micron
429 g/mil
ASTM D1922
Dart Drop Test 165 g
0.364 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 31.0 MPa
4500 psi
ASTM D882
Film Tensile Strength at Break, TD 27.0 MPa
3920 psi
ASTM D882
Optical Properties Metric English Comments
Haze 9.5 %
9.5 %
ASTM D1003
Gloss 115 %
115 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 180 - 190 °C
356 - 374 °F
Plasticizing Zone
190 - 200 °C
374 - 392 °F
Mixture Zone
Feed Temperature 180 - 190 °C
356 - 374 °F
Adapter Temperature 200 - 215 °C
392 - 419 °F
Die Opening 0.180 - 0.250 cm
0.0709 - 0.0984 in
Blow-up Ratio (BUR) 3.0
3.0
Recommended
Descriptive Properties Value Comments
Proportion LLDPE % 75
PTN-570-Q