Permabond UV610 UV-curable Adhesive

Category Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer Permabond
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Permabond UV610 UV-curable Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PERMABOND UV610 is a single part, fast setting, UV curable adhesive designed specifically for bonding glass and metal. Its high strength makes it suitable for a wide range of applications including glass furniture where it is possible to create high strength edge joints. Features & Benefits: Cure on demand High shear strength Fast curing with low power lamps 100% solids, no solvents Excellent adhesion to metal and glass Information provided by Permabond.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
uncured
Viscosity 800 - 1000 cP

@Temperature 25.0 °C
800 - 1000 cP

@Temperature 77.0 °F
Uncured
Storage Temperature 5.00 - 25.0 °C
41.0 - 77.0 °F
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
Tensile Strength 17.0 MPa
2470 psi
ASTM D2095
Elongation at Break 95 %
95 %
Adhesive Bond Strength 13.0 - 16.0 MPa
1890 - 2320 psi
Glass/steel, Shear
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Minimum Service Temperature, Air -53.9 °C
-65.0 °F
Optical Properties Metric English Comments
Refractive Index 1.47
1.47
Electrical Properties Metric English Comments
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz,
Temperature 25.0 °C
4.0

@Frequency 1.00e+6 Hz,
Temperature 77.0 °F
Dielectric Strength 12.0 kV/mm
305 kV/in
Processing Properties Metric English Comments
Cure Time 0.183 min
0.00306 hour
fixture time, (low power 4mW lamp)
Shelf Life 12.0 Month
12.0 Month
Descriptive Properties Value Comments
Appearance Translucent
Uncured
Cure Wavelength (nm) 365-400
Maximum Gap Fill (mm) 0.3
Strength Retention 10% at 200°C
Relative to 0°C
100% at 0°C
Relative to 0°C
30% at 150°C
Relative to 0°C
75% at 100°C
Relative to 0°C
95% at 50°C
Relative to 0°C