Permabond LH150 Anaerobic Threadsealant

Category Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer Permabond
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Permabond LH150 Anaerobic Threadsealant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Permabond® LH150 Pipe Sealant with PTFE is designed for sealing and locking tapered metal pipe threads and fittings. It is ideal for stainless steel and other passive metals. Instant sealing of up to 1000 psi is achieved upon limited hand tightening. After cure, the sealing capability is up to the burst rating on the typical pipe. The low locking strength allows easy disassembly. UL Classification: Permabond LH150 is classified by Underwriters Laboratories Inc. ® for use in devices handling gasoline, petroleum oils, and natural gas (pressure not over 100 psig) propane and butane not exceeding 2 in. Features & Benefits: Full cure seal to the burst rating of pipe Easy to use and apply Directional freedom Does not contain solvents Excellent chemical and temperature resistance Cures at room temperature Will not shred, tear or cause blockages Information provided by Permabond.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Uncured
Viscosity 260000 cP

@Temperature 25.0 °C
260000 cP

@Temperature 77.0 °F
Uncured
Storage Temperature 5.00 - 25.0 °C
41.0 - 77.0 °F
Mechanical Properties Metric English Comments
Adhesive Bond Strength 7.00 MPa
1020 psi
steel collar and pin shear; ISO 10123
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
Thermal Conductivity 0.190 W/m-K
1.32 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 177 °C
350 °F
Minimum Service Temperature, Air -53.9 °C
-65.0 °F
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 23.0 °C
1.00 hour

@Temperature 73.4 °F
Brass, handling strength
60.0 min

@Temperature 23.0 °C
1.00 hour

@Temperature 73.4 °F
Zinc, handling strength
120 min

@Temperature 23.0 °C
2.00 hour

@Temperature 73.4 °F
M10 steel, handling strength
180 min

@Temperature 23.0 °C
3.00 hour

@Temperature 73.4 °F
Stainless steel, handling strength
180 - 360 min

@Temperature 23.0 °C
3.00 - 6.00 hour

@Temperature 73.4 °F
Brass, working strength
180 - 360 min

@Temperature 23.0 °C
3.00 - 6.00 hour

@Temperature 73.4 °F
M10 steel, working strength
360 min

@Temperature 23.0 °C
6.00 hour

@Temperature 73.4 °F
Zinc, working strength
1440 min

@Temperature 23.0 °C
24.0 hour

@Temperature 73.4 °F
M10 steel, full strength
Shelf Life 12.0 Month
12.0 Month
Descriptive Properties Value Comments
Appearance White
Uncured
Maximum Gap Fill (mm) 0.5
Strength Retention 20% at 200°C
Relative to 0°C
60% at 150°C
Relative to 0°C
85% at 100°C
Relative to 0°C
93% at 50°C
Relative to 0°C
Torque Strength (N m) 3
M10 steel, prevail
6
M10 steel, break