Permabond ES562 Epoxy Resin

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Permabond
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Permabond ES562 Epoxy Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PERMABOND® ES562 is a single-part epoxy adhesive which flows like solder when heated during curing. The adhesive has excellent adhesion to metal surfaces and composites. The high bond strength of this adhesive allows it to replace mechanical fastening, soldering or brazing. The adhesive’s low viscosity is such that it self-levels. Features & Benefits: Excellent adhesive strength Excellent resistance to vibration Easy to use – no mixing required High shear strength High temperature resistance Good resistance to chemicals Information provided by Permabond.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
Uncured
Viscosity 15000 - 30000 cP

@Temperature 25.0 °C
15000 - 30000 cP

@Temperature 77.0 °F
Uncured
Storage Temperature 2.00 - 7.00 °C
35.6 - 44.6 °F
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
ISO 868
Adhesive Bond Strength 14.0 - 27.0 MPa
2030 - 3920 psi
Aluminum, Shear; ISO 4587
14.0 - 27.0 MPa
2030 - 3920 psi
Zinc, Shear; ISO 4587
20.0 - 35.0 MPa
2900 - 5080 psi
Steel , Shear; ISO 4587
Thermal Properties Metric English Comments
CTE, linear 45.0 µm/m-°C
25.0 µin/in-°F
Thermal Conductivity 0.550 W/m-K
3.82 BTU-in/hr-ft²-°F
Processing Properties Metric English Comments
Cure Time <= 3.00 min
<= 0.0500 hour
Induction
30.0 min

@Temperature 150 °C
0.500 hour

@Temperature 302 °F
Oven
45.0 min

@Temperature 120 °C
0.750 hour

@Temperature 248 °F
Oven
Shelf Life 6.00 Month
6.00 Month
Descriptive Properties Value Comments
Appearance White
Uncured
Maximum Gap Fill (mm) 0.25
Strength Retention 100% at 0°C
Relative to 0°C
25% at 200°C
Relative to 0°C
65% at 150°C
Relative to 0°C
85% at 100°C
Relative to 0°C
95% at 50°C
Relative to 0°C