Parker Chomerics Tecknit Teckfip™ FIP-X Formed in Place Conductive Elastomer

Category	Polymer
Manufacturer	Parker Chomerics Tecknit
Trade Name	Teckfip™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics Tecknit Teckfip™ FIP-X Formed in Place Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: FIP-X is Tecknit’s newest compound and features a conductive powder that is a unique particle combining tungsten carbide and aluminum. The premium advantage of this compound is its ability to be non-corrosive even in the most hostile of external environments. The compound has been exhaustively tested for hostile environments and easily exceeds the requirements of the ASTM B117 test specification. Tecknit also offers a flame-retardant version of this compound which has achieved the UL94-V0 rating.Information provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	1.479 - 2.001 g/cc	1.479 - 2.001 g/cc

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	57 - 73	57 - 73
Tensile Strength	1.48 MPa	215 psi
Elongation at Break	>= 90 %	>= 90 %
Peel Strength	>= 9.00 kN/m	>= 51.4 pli
Compression Set	25 %	25 %	Recommended
	10 - 50 %	10 - 50 %
	31 % @Temperature 70.0 °C, Time 79200 sec	31 % @Temperature 158 °F, Time 22.0 hour

Thermal Properties	Metric	English
Maximum Service Temperature, Air	125 °C	257 °F
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	0.031 ohm-cm	0.031 ohm-cm
Surface Resistance	1.5 ohm	1.5 ohm	[ohm-cm]
	0.046 ohm @Temperature 85.0 °C, Time 605000 sec	0.046 ohm @Temperature 185 °F, Time 168 hour

Processing Properties	Metric	English	Comments
Dry Time	>= 0.200 hour	>= 0.200 hour	Tack Free
Cure Time	<= 1440 min	<= 24.0 hour
Shelf Life	1.00 Month	1.00 Month	Syringe
	6.00 Month	6.00 Month	Cartridge

Descriptive Properties	Value	Comments
Color	Dark Gray
Filler	Tungsten Carbide