Parker Chomerics CHO-SEAL S6305 Conductive Elastomer

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone
Manufacturer	Parker Chomerics
Trade Name	CHO-SEAL
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics CHO-SEAL S6305 Conductive Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Good performance in moderately corrosive environments; material of choice for flange finishes needing “bite-through” for good electrical contact.Molded and Extruded.RoHS CompliantInformation provided by Chomerics

Physical Properties	Metric	English	Comments
Specific Gravity	1.75 - 2.25 g/cc	1.75 - 2.25 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55 - 75	55 - 75	ASTM D2240
Tensile Strength at Break	>= 1.38 MPa	>= 200 psi	ASTM D412
Tensile Strength	1.40 MPa	203 psi	Test 2; ASTM D412
	1.19 MPa @Temperature 22.0 °C, Time 252000 sec	172 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Vinyl Protectant; ASTM D412
	1.21 MPa @Temperature 22.0 °C, Time 252000 sec	175 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Tire Cleaner; ASTM D412
	1.23 MPa @Temperature 22.0 °C, Time 252000 sec	178 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to ClearVue®; ASTM D412
	1.36 MPa @Temperature 22.0 °C, Time 252000 sec	197 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Formula 409®; ASTM D412
	1.37 MPa @Temperature 22.0 °C, Time 252000 sec	199 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Cola; ASTM D412
	1.37 MPa @Temperature 22.0 °C, Time 252000 sec	199 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Tap Water; ASTM D412
	1.39 MPa @Temperature 22.0 °C, Time 252000 sec	202 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Windex®; ASTM D412
	1.43 MPa @Temperature 22.0 °C, Time 252000 sec	207 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Carpet Cleaner; ASTM D412
	1.43 MPa @Temperature 22.0 °C, Time 252000 sec	207 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Hairspray; ASTM D412
	1.43 MPa @Temperature 22.0 °C, Time 252000 sec	207 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Windshield Washer Solvent; ASTM D412
	1.45 MPa @Temperature 22.0 °C, Time 252000 sec	211 psi @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Coffee; ASTM D412
Elongation at Break	>= 100 %	>= 100 %	ASTM D412
	289 %	289 %	Test 1; ASTM D412
	414 %	414 %	Test 2; ASTM D412
	166 % @Temperature 22.0 °C, Time 252000 sec	166 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Windex®; ASTM D412
	219 % @Temperature 22.0 °C, Time 252000 sec	219 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Formula 409®; ASTM D412
	317 % @Temperature 22.0 °C, Time 252000 sec	317 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to ClearVue®; ASTM D412
	326 % @Temperature 22.0 °C, Time 252000 sec	326 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Hairspray; ASTM D412
	418 % @Temperature 22.0 °C, Time 252000 sec	418 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Tire Cleaner; ASTM D412
	418 % @Temperature 22.0 °C, Time 252000 sec	418 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Windshield Washer Solvent; ASTM D412
	433 % @Temperature 22.0 °C, Time 252000 sec	433 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Vinyl Protectant; ASTM D412
	433 % @Temperature 22.0 °C, Time 252000 sec	433 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Cola; ASTM D412
	439 % @Temperature 22.0 °C, Time 252000 sec	439 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Coffee; ASTM D412
	439 % @Temperature 22.0 °C, Time 252000 sec	439 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Tap Water; ASTM D412
	443 % @Temperature 22.0 °C, Time 252000 sec	443 % @Temperature 71.6 °F, Time 70.0 hour	50% RH, Exposure to Carpet Cleaner; ASTM D412
Tear Strength	8.75 kN/m	49.9 pli	ASTM D624
Compression Set	<= 30 % @Temperature 100 °C, Time 252000 sec	<= 30 % @Temperature 212 °F, Time 70.0 hour	ASTM D395 Method B

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.800 W/m-K @Pressure 2.07 MPa	5.55 BTU-in/hr-ft²-°F @Pressure 300 psi	ASTM D5470
Maximum Service Temperature, Air	150 °C	302 °F
Minimum Service Temperature, Air	-45.0 °C	-49.0 °F	Flex TR10; ASTM D1329
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	0.10 ohm-cm	0.10 ohm-cm	as supplied without pressure sensitive adhesive; CEPS-0002
Shielding Effectiveness	>= 75 dB @Frequency 4.00e+10 Hz	>= 75 dB @Frequency 4.00e+10 Hz	E Field; CHO-TM-TP08
	>= 100 dB @Frequency 1.00e+8 Hz	>= 100 dB @Frequency 1.00e+8 Hz	E Field; CHO-TM-TP08
	>= 100 dB @Frequency 5.00e+8 Hz	>= 100 dB @Frequency 5.00e+8 Hz	Plane Wave; CHO-TM-TP08
	>= 100 dB @Frequency 2.00e+9 Hz	>= 100 dB @Frequency 2.00e+9 Hz	Plane Wave; CHO-TM-TP08
	>= 100 dB @Frequency 1.00e+10 Hz	>= 100 dB @Frequency 1.00e+10 Hz	Plane Wave; CHO-TM-TP08

Descriptive Properties	Value	Comments
Binder	Silicone
Filler	Ni/C
Heat Aging	<0.25 ohm-cm	125°C for 48 hrs; CEPS-0002