Parker Chomerics CHO-BOND 1038 Conductive Silicone RTV Adhesive

Category	Polymer , Adhesive , Thermoset , Silicone
Manufacturer	Parker Chomerics
Trade Name	CHO-BOND
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Parker Chomerics CHO-BOND 1038 Conductive Silicone RTV Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Electrically conductive, one component silicone adhesive/sealant that may be used for bonding EMI gaskets or for providing EMI and environmental protection as a caulk. This material cures on exposure to atmospheric moisture, and contains no acetic acid or other corrosive agents.Information provided by Chomerics

Physical Properties	Metric	English
Specific Gravity	3.20 - 3.90 g/cc	3.20 - 3.90 g/cc
Volatile Organic Compounds (VOC) Content	117 g/l	117 g/l
Thickness	>= 178 microns	>= 7.00 mil

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	>= 55	>= 55
Shear Strength	1.03 MPa	150 psi	Lap; 2.5cm aluminum strips, 13mm overlap, 0.25mm thick adhesive layer
Peel Strength	0.440 kN/m	2.51 pli	12.7mm bond width on aluminum strips 0.127mm thick pulled at 51 cm/min

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	125 °C	257 °F
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 0.010 ohm-cm	<= 0.010 ohm-cm

Processing Properties	Metric	English	Comments
Cure Time	10100 min @Temperature 23.0 °C	168 hour @Temperature 73.4 °F
Shelf Life	6.00 Month	6.00 Month

Descriptive Properties	Value	Comments
Consistency	Medium Paste
Coverage	10.6 cm² / g
	50	(3.2mm diam. Bead) ft/lb
Mix Ratio	1-part
Working Life	0.5 hr