Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 6K 4HS IM7 Reinforced

Category Polymer , Thermoset , Epoxy
Manufacturer Park Electrochemical Corp.
Trade Name Nelcote®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 6K 4HS IM7 Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request.Key Features and Benefits:Designed to replace first generation 350°F (176°C) cure systems.Wide cure temperature process window of 250°F to 350°FExhibits very low void content, i.e.,
Mechanical Properties Metric English Comments
Tensile Strength, Yield 903 MPa

@Temperature 21.1 °C
 131000 psi

@Temperature 70.0 °F
 0° Direction, Dry; Autoclave Cured; ASTM D3039-95
Tensile Modulus 75.8 GPa

@Temperature 21.1 °C
 11000 ksi

@Temperature 70.0 °F
 0° Direction, Dry; Autoclave Cured; ASTM D3039-95
Compressive Strength 531 MPa

@Temperature 82.2 °C
 77000 psi

@Temperature 180 °F
 Wet; Autoclave Cured; SACMA 1-94
607 MPa

@Temperature 82.2 °C
 88000 psi

@Temperature 180 °F
 Dry; Autoclave Cured; SACMA 1-94
758 MPa

@Temperature 21.1 °C
 110000 psi

@Temperature 70.0 °F
 Dry; Autoclave Cured; SACMA 1-94
Compressive Modulus 62.1 GPa

@Temperature 82.2 °C
 9000 ksi

@Temperature 180 °F
 Dry; Autoclave Cured; SACMA 1-94
65.5 GPa

@Temperature 21.1 °C
 9500 ksi

@Temperature 70.0 °F
 Dry; Autoclave Cured; SACMA 1-94
76.5 GPa

@Temperature 82.2 °C
 11100 ksi

@Temperature 180 °F
 Wet; Autoclave Cured; SACMA 1-94
Shear Strength 47.6 MPa

@Temperature 82.2 °C
 6900 psi

@Temperature 180 °F
 Beam, V-Notched; Wet; Autoclave Cured; ASTM D5379-93
50.3 MPa

@Temperature 82.2 °C
 7300 psi

@Temperature 180 °F
 Short-Beam, Wet; Autoclave Cured; ASTM D2344
52.4 MPa

@Temperature 82.2 °C
 7600 psi

@Temperature 180 °F
 Beam, V-Notched; Dry; Autoclave Cured; ASTM D5379-93
62.1 MPa

@Temperature 21.1 °C
 9000 psi

@Temperature 70.0 °F
 Beam, V-Notched; Dry; Autoclave Cured; ASTM D5379-93
64.1 MPa

@Temperature 82.2 °C
 9300 psi

@Temperature 180 °F
 Short-Beam, Dry; Autoclave Cured; ASTM D2344
71.0 MPa

@Temperature 21.1 °C
 10300 psi

@Temperature 70.0 °F
 Short-Beam, Dry; Autoclave Cured; ASTM D2344
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature -17.8 °C
 6.00 Month

@Temperature 0.000 °F
Descriptive Properties Value Comments
Fabric Area Weight (g/m²) 203