Park Electrochemical Nelco® N4000-7 SI® FR-4 Epoxy Laminate and Prepreg

Category	Polymer , Thermoset , Epoxy
Manufacturer	Park Electrochemical Corp.
Trade Name	Nelco®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Park Electrochemical Nelco® N4000-7 SI® FR-4 Epoxy Laminate and Prepreg.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Nelco® N4000-7 low-CTE epoxy laminate and prepreg system is a cost-effective solution for use in a broad range of multilayer PCB designs requiring low Z-axis expansion, excellent thermal stability and superior hole-wall integrity.Key Features and Benefits:Outstanding Z-axis, thermal stability and hole wall integrityAutomotive TestingSI (Signal Integrity) optionCAF resistantCost-effective standard FR-4 processingApplications/Qualifications:Wireless HandsetsWireless InfrastructureDigital Broadband MultilayersAutomotiveUnderhood AutomotiveBackplanesFine-Line MultilayersFine Pitch BGA MultilayersDirect Chip AttachRoHS CompliantMeets IPC-4101/98 SpecificationsInformation provided by Park Electrochemical Corp.

Physical Properties	Metric	English	Comments
Density	1.97 g/cc	0.0712 lb/in³	50% Resin Content; Internal Method
Water Absorption	0.070 %	0.070 %	IPC-TM-650.2.6.2.1

Mechanical Properties	Metric	English	Comments
Peel Strength	1.31 kN/m	7.50 pli	after solder float; IPC-TM-650.2.4.8
	1.42 kN/m	8.10 pli	at elevated temperature; IPC-TM-650.2.4.8.2a
	1.58 kN/m	9.00 pli	after exposure to process solutions; IPC-TM-650.2.4.8

Thermal Properties	Metric	English	Comments
CTE, linear	12.0 - 15.0 µm/m-°C @Temperature -40.0 - 125 °C	6.67 - 8.33 µin/in-°F @Temperature -40.0 - 257 °F	X/Y; IPC-TM-650.2.4.41
	50.0 µm/m-°C @Temperature 50.0 - 155 °C	27.8 µin/in-°F @Temperature 122 - 311 °F	Z-Axis Alpha 1; IPC-TM-650.2.4.41
	270 µm/m-°C @Temperature 155 - 260 °C	150 µin/in-°F @Temperature 311 - 500 °F	Z-Axis Alpha 2; IPC-TM-650.2.4.41
Specific Heat Capacity	1.21 J/g-°C	0.290 BTU/lb-°F	ASTM E1461
Thermal Conductivity	0.525 W/m-K	3.64 BTU-in/hr-ft²-°F	ASTM E1461
Glass Transition Temp, Tg	150 °C	302 °F	TMA; IPC-TM-650.2.4.24c
	155 °C	311 °F	DSC; IPC-TM-650.2.4.25c
	160 °C	320 °F	DMA (Tan d Peak); IPC-TM-650.2.4.24.3
Decomposition Temperature	330 °C	626 °F	5% weight loss; TGA; IPC-TM-650.2.4.24.6
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	E - 24/125; IPC-TM-650.2.5.17.1
	1.00e+14 ohm-cm	1.00e+14 ohm-cm	C - 96/35/90; IPC-TM-650.2.5.17.1
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	E - 24/125; IPC-TM-650.2.5.17.1
	1.00e+14 ohm	1.00e+14 ohm	C - 96/35/90; IPC-TM-650.2.5.17.1
Dielectric Constant	3.3 @Frequency 1.00e+10 Hz	3.3 @Frequency 1.00e+10 Hz	Stripline; IPC-TM-650.2.5.5.5
	3.4 @Frequency 2.50e+9 Hz	3.4 @Frequency 2.50e+9 Hz	Stripline; IPC-TM-650.2.5.5.5
	3.6 @Frequency 1.00e+9 Hz	3.6 @Frequency 1.00e+9 Hz	RF Impedance; IPC-TM-650.2.5.5.9
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	TFC/LCR Meter; IPC-TM-650.2.5.5.3
Dielectric Strength	49.2 kV/mm	1250 kV/in	IPC-TM-650.2.5.6.2
Dielectric Breakdown	>= 50000 V	>= 50000 V	IPC-TM-650.2.5.6
Dissipation Factor	0.015 @Frequency 2.50e+9 Hz	0.015 @Frequency 2.50e+9 Hz	Stripline; IPC-TM-650.2.5.5.5
	0.016 @Frequency 1.00e+10 Hz	0.016 @Frequency 1.00e+10 Hz	Stripline; IPC-TM-650.2.5.5.5
	0.016 @Frequency 1.00e+6 Hz	0.016 @Frequency 1.00e+6 Hz	TFC/LCR Meter; IPC-TM-650.2.5.5.3
Arc Resistance	124 sec	124 sec	IPC-TM-650.2.5.1

Descriptive Properties	Value	Comments
Methylene Chloride Resistance (% Weight Change)	0.31	IPC-TM-650.2.3.4.3
Pressure Cooker	Pass	60 min then solder dip @288ºC until failure (max 10 min.); IPC-TM-650.2.6.16 (modified)
T260 (minutes)	16	IPC-TM-650.2.4.24.1
Z Axis Expansion (%)	3.7	50ºC to 260ºC; IPC-TM-650.2.4.41