Palm Labs Adhesives TURBO-LOCK SERIES 11-OR Anaerobic Thread Locking Compound

Category Polymer , Adhesive , Thermoset , Methacrylate , Methacrylate Adhesive
Manufacturer Palm Labs Adhesives
Trade Name TURBO-LOCK SERIES
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Palm Labs Adhesives TURBO-LOCK SERIES 11-OR Anaerobic Thread Locking Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TURBO-LOCK 11-OR SERIES is a fast curing, BLUE, removable, medium strength, oil resistant, primerless, general purpose anaerobic thread-locking compound for bonding and sealing threads. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbons and many chemicals. Disassembles with hand tools.Applications:Ideal for less active materials such as stainless steel and plated parts.Ideal for thread locking plated parts, vibration or moving components.Ideal for fasteners between up to ¾” (up to 20 mm) diameters.Locks and seals threaded joints-nuts, screws, and studs with improved oil resistance.Part Numbers for this data: 11-000-OR, 11-001-OR, 11-010-OR, 11-050-OR, 11-250-OR, 11-1000-ORInformation provided by Palm Laboratories Adhesives
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
Brookfield Viscosity 2250 cP
2250 cP
RVT Spindle 3 @ 20 rpm
Mechanical Properties Metric English Comments
Shear Strength >= 8.00 MPa
>= 1160 psi
Steel pins and collars; ISO 10964
Thermal Properties Metric English Comments
CTE, linear 0.800 µm/m-°C
0.444 µin/in-°F
ASTM D696
Specific Heat Capacity 0.300 J/g-°C
0.0717 BTU/lb-°F
Thermal Conductivity 0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
ASTM C177
Flash Point >= 37.8 °C
>= 100 °F
Processing Properties Metric English Comments
Cure Time 60.0 - 180 min
1.00 - 3.00 hour
Functional
1440 min
24.0 hour
Full
10.0 - 12.0 min

@Temperature -55.0 - 150 °C
0.167 - 0.200 hour

@Temperature -67.0 - 302 °F
Handling
Shelf Life 24.0 Month
24.0 Month
Descriptive Properties Value Comments
Appearance Blue
Chemical Resistance 100% Initial Strength Retained
Ethanol at 22°C, at 500hrs
100% Initial Strength Retained
Gasoline at 22°C, at 500hrs
100% Initial Strength Retained
Brake Fluid at 22°C, at 500hrs
100% Initial Strength Retained
Ethanol at 22°C, at 1000hrs
100% Initial Strength Retained
Gasoline at 22°C, at 1000hrs
100% Initial Strength Retained
Brake Fluid at 22°C, at 1000hrs
80% Initial Strength Retained
Water/Glycol at 87°C, at 1000hrs
90% Initial Strength Retained
Water/Glycol at 87°C, at 500hrs
90% Initial Strength Retained
Acetone at 22°C, at 1000hrs
95% Initial Strength Retained
Motor Oil at 125°C, at 1000hrs
95% Initial Strength Retained
Motor Oil at 125°C, at 500hrs
95% Initial Strength Retained
Acetone at 22°C, at 500hrs
Composition Dimethacrylate Ester
Max Screw Size 3/4” / 20 mm
Torque 20 N.m
Breakaway, M10 steel nuts and bolts N.m, ISO 10964
24 N.m
Breakloose, pre-torqued to 5 N.m, M10 steel nuts and bolts, ISO 10964
24 N.m
Max Prevail, pre-torqued to 5 N.m, M10 steel nuts and bolts N.m, ISO 10964
7 N.m
Prevail, M10 steel nuts and bolts N.m, ISO 10964