Palm Labs Adhesives TURBO FUSE METHYL FOR METALS (75-95 Viscosity) Rapid Bonding Adhesive

Category Polymer , Adhesive
Manufacturer Palm Labs Adhesives
Trade Name TURBO FUSE METHYL FOR METALS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Palm Labs Adhesives TURBO FUSE METHYL FOR METALS (75-95 Viscosity) Rapid Bonding Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Palm Lab's Methyl Cyanoacrylate is a one component rapid bonding adhesive ideal for metal surfaces. TURBO FUSE METHYL’s advanced formula is designed to polymerize instantly by absorbing surface moisture and is specifically formulated to bond various metals including aluminum, stainless steel, and copper, to itself and to a variety of materials including wood, balsa wood, rubber, plastics and leather. Applications include wiper blades, nameplates, gearshift indicators, aerospace parts, automotive and machinery parts, electronic components, transportation equipment, etc. Meets MLLA 46050 Type I Class II specification requirements.Part Numbers for this data: 15-080Methyl, 30-080MethylSoluble in Acetone, MEK, Amide, Methylene ChlorideInformation provided by Palm Laboratories Adhesives
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
Liquid State
Viscosity 75 - 95 cP
75 - 95 cP
Liquid State
Mechanical Properties Metric English Comments
Shear Strength >= 5.00 MPa
>= 725 psi
ABS; ASTM D1002/DIN 53283
>= 10.0 MPa
>= 1450 psi
Polycarbonate; ASTM D1002/DIN 53283
>= 13.0 MPa
>= 1890 psi
Copper; ASTM D1002/DIN 53283
13.0 - 20.0 MPa
1890 - 2900 psi
Tensile, (Cured State)
>= 20.0 MPa
>= 2900 psi
Grit Blasted Steel; ASTM D1002/DIN 53283
>= 20.0 MPa
>= 2900 psi
Etched Aluminum; ASTM D1002/DIN 53283
>= 20.0 MPa
>= 2900 psi
Stainless Steel; ASTM D1002/DIN 53283
Thermal Properties Metric English Comments
CTE, linear 1.00 µm/m-°C
0.556 µin/in-°F
ASTM D696
Melting Point 160 - 170 °C
320 - 338 °F
Cured State
Maximum Service Temperature, Air 26.7 °C
80.0 °F
Cured State
Minimum Service Temperature, Air -51.1 °C
-60.0 °F
Cured State
Glass Transition Temp, Tg 120 °C
248 °F
ASTM E228
Flash Point 80.0 - 93.3 °C
176 - 200 °F
Liquid State
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 2.3
2.3
Cured State; ASTM D150
Dielectric Strength 24.98 kV/mm
634.5 kV/in
Cured; ASTM D149
Processing Properties Metric English Comments
Cure Time 1440 min
24.0 hour
Cured State
Shelf Life 12.0 Month
12.0 Month
Liquid State
Descriptive Properties Value Comments
Appearance Clear liquid
Liquid State
Clear-Hard
Cured State
Base compound (Resin) Methyl Cyanoacrylate
Liquid State
Chemical Resistance 75% Initial Strength Retained
Gasoline at 22°C, at 1000hrs
80% Initial Strength Retained
Gasoline at 22°C, at 500hrs
85% Initial Strength Retained
Isopropanol at 22°C, at 500hrs
85% Initial Strength Retained
Isopropanol at 22°C, at 1000hrs
90% Initial Strength Retained
Motor Oil at 40°C, at 500hrs
90% Initial Strength Retained
Mineral Spirit at 22°C, at 500hrs
90% Initial Strength Retained
Motor Oil at 40°C, at 1000hrs
90% Initial Strength Retained
Mineral Spirit at 22°C, at 1000hrs
Gap Fill 0.20 mm
Cured State
Material Set Up Time 10-15 sec
SBR to SBR
10-20 sec
Copper to Copper
10-30 sec
Steel to Steel
15-20 sec
Steel to PVC
30-60 sec
Stainless Steel to Stainless Steel
3-10 sec
PVC to PVC
40-60 sec
Aluminum to Aluminum