- PTS Tristar® PC-05GFR 5% Glass Reinforced Polycarbonate With Release
PTS Tristar® PC-05GFR 5% Glass Reinforced Polycarbonate With Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-05GFR 5% Glass Reinforced Polycarbonate With Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa @Thickness 3.17 mm |
8500 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 15 % @Thickness 3.17 mm |
15 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Yield Strength | 93.1 MPa @Thickness 3.17 mm |
13500 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.48 GPa @Thickness 3.17 mm |
360 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm |
2.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| UL RTI, Electrical | 125 °C | 257 °F | |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | PLC 7 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC 3 |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC 2 |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | PLC 0 |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Middle Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Front Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |
| Nozzle Temperature | 249 - 288 °C | 480 - 550 °F | |
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed- Edge Gate | Fast | |
| Injection Speed- Tab Gate | Fast | |
| Injection Speed- Tunnel Gate | Fast |
Users viewing this material also viewed the following:
- Nye Lubricants 230A (SO) Synthetic Oil
- Lehmann & Voss LUVOCOM® 1301-7294/BL PPS, linear, with glass fiber
- Hyosung Topilene B301 PP
- Special Metals INCOLOY® alloy 832 Stainless Steel
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 40-HR-9 TPE
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Wellman Wellamid® GF13-66 XE-NBK1 13% Glass Fiber Reinforced, Engineering Grade Nylon 66
- Zircar Zirconia HfF-15 Hafnia Knit Textile Insulation
- NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved