PTS Trilac® FR3800 Flame Retardant ABS Resin, RoHS Compliant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Trilac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Trilac® FR3800 Flame Retardant ABS Resin, RoHS Compliant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Melt Flow 8.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 8.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength 37.9 MPa

@Thickness 3.17 mm
 5500 psi

@Thickness 0.125 in
 ASTM D638
Flexural Strength 65.5 MPa

@Thickness 3.17 mm
 9500 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.24 GPa

@Thickness 3.17 mm
 325 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 1.44 J/cm

@Thickness 6.35 mm
 2.70 ft-lb/in

@Thickness 0.250 in
 ASTM D256
1.60 J/cm

@Thickness 3.17 mm
 3.00 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 83.3 °C
182 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL file E155285
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 171 - 182 °C
340 - 360 °F
Middle Barrel Temperature 199 - 210 °C
390 - 410 °F
Front Barrel Temperature 204 - 216 °C
400 - 420 °F
Nozzle Temperature 204 - 216 °C
400 - 420 °F
Melt Temperature 193 - 232 °C
380 - 450 °F
Mold Temperature 54.4 - 71.1 °C
130 - 160 °F
Drying Temperature 87.8 °C
190 °F
max 6 hours
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 55.2 - 82.7 MPa
8000 - 12000 psi
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Shot Size 50 - 80 %
50 - 80 %
Vent Depth 0.00381 - 0.00762 cm
0.00150 - 0.00300 in
Screw Speed 30 - 60 rpm
30 - 60 rpm