Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

PTS PCA-2201NH Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS PCA-2201NH Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Linear Mold Shrinkage 0.004 - 0.006 cm/cm
0.004 - 0.006 in/in
ASTM D955
Melt Flow 12 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 12 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
16 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa

@Thickness 3.17 mm
 8700 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 65 %

@Thickness 3.17 mm
 65 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 88.9 MPa

@Thickness 3.17 mm
 12900 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.69 GPa

@Thickness 3.17 mm
 390 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 5.87 J/cm

@Thickness 3.17 mm
 11.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
UL RTI, Electrical 60.0 °C
140 °F
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL RTI, Mechanical without Impact 60.0 °C
140 °F
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 all colors; UL file E155285
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
 all colors; UL file E155285
5VA

@Thickness 2.50 mm
 5VA

@Thickness 0.0984 in
5VA

@Thickness 3.0 mm
 5VA

@Thickness 0.12 in
 all colors; UL file E155285
Glow Wire Test 700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWIT; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 GWIT; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 GWIT; IEC 60695-2-13
925 °C

@Thickness 1.50 mm
 1700 °F

@Thickness 0.0591 in
 GWFI; IEC 60695-2-12
925 °C

@Thickness 2.00 mm
 1700 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
950 °C

@Thickness 3.00 mm
 1740 °F

@Thickness 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 18.0 kV/mm
457 kV/in
Comparative Tracking Index >= 600 V
>= 600 V
PLC 0
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 1.50 mm
 15 - 30 sec

@Thickness 0.0591 in
 PLC 3
15 - 30 sec

@Thickness 2.50 mm
 15 - 30 sec

@Thickness 0.0984 in
 PLC 3
30 - 60 sec

@Thickness 3.00 mm
 30 - 60 sec

@Thickness 0.118 in
 PLC 2
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
 PLC 1
60 - 120 arcs

@Thickness 2.50 mm
 60 - 120 arcs

@Thickness 0.0984 in
 PLC 1
60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 PLC 1
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC 3
Users viewing this material also viewed the following: