PTS PCA-2008 Flame Retardant PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS PCA-2008 Flame Retardant PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Water Absorption 0.10 %
0.10 %
24 Hr.; ASTM D570
Melt Flow 16 g/10 min

@Load 2.20 kg,
Temperature 260 °C
 16 g/10 min

@Load 4.85 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.2 MPa

@Thickness 3.17 mm
 8000 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 40 %

@Thickness 3.17 mm
 40 %

@Thickness 0.125 in
 ASTM D638
Flexural Strength 89.6 MPa

@Thickness 3.17 mm
 13000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.17 mm
 370 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 4.27 J/cm

@Thickness 3.17 mm
 8.00 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
ASTM D648
UL RTI, Electrical 60.0 °C
140 °F
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL RTI, Mechanical without Impact 60.0 °C
140 °F
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VB

@Thickness 3.00 mm
 5VB

@Thickness 0.118 in