PTS 15GFR-BK PBT- Flame Retardant, 15% Glass Filled PBT Black Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS 15GFR-BK PBT- Flame Retardant, 15% Glass Filled PBT Black Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.1 MPa @Thickness 3.17 mm |
13800 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 2.5 % @Thickness 3.17 mm |
2.5 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 148 MPa @Thickness 3.17 mm |
21500 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 5.17 GPa @Thickness 3.17 mm |
750 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| UL RTI, Electrical | 75.0 °C | 167 °F | |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA 6 - Akulon 6 - Dry
- PolyChem Alloy FlexGel 3137KS TPE
- DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin
- ExxonMobil Escorene™ UL 00218CC3 Ethylene Vinyl Acetate Copolymer (European Grade)
- CP-Polymer-Technik Wellamid® 6000/51 GV 30 HWCP 30% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned
- CIMBAR Miti-Wite B1 Chemically Purified White Barite (BaSO4)
- Dow Nordel® NDR 47130.01 EPDM Hydrocarbon Rubber
- Arlon 0.011" (0.2794 mm) Uncured Silicone Traction Motor Insulation (P29600R011)
- Bulk Molding Compounds BMC T15(F) High Strength Grade Molding Compound
- LG Chemical LUPOY NS5000C PC/ABS, High Impact
Copyright © lookpolymers.com All Rights Reserved