- PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T4
PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T4
| Category | Metal , Nonferrous Metal , Aluminum Alloy |
| Manufacturer | PEAK Werkstoff |
| Trade Name | DISPAL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T4.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High stiffness and elongation at rupture. Property data for Condition T4 (Quench in water at RT).Information provided by PEAK Werkstoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.679 - 2.961 g/cc | 0.09679 - 0.1070 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | >= 125 | >= 125 | |
| Tensile Strength | >= 488 MPa | >= 70800 psi | |
| Tensile Strength, Yield | >= 334 MPa | >= 48400 psi | |
| Elongation at Break | >= 16 % | >= 16 % | |
| Modulus of Elasticity | >= 72.0 GPa | >= 10400 ksi | |
| >= 58.0 GPa @Temperature 300 °C |
>= 8410 ksi @Temperature 572 °F |
Condition T6 | |
| >= 65.0 GPa @Temperature 200 °C |
>= 9430 ksi @Temperature 392 °F |
Condition T6 | |
| Poissons Ratio | 0.341 @Temperature 20.0 °C |
0.341 @Temperature 68.0 °F |
Condition T6 |
| 0.347 @Temperature 100 °C |
0.347 @Temperature 212 °F |
Condition T6 | |
| 0.354 @Temperature 150 °C |
0.354 @Temperature 302 °F |
Condition T6 | |
| 0.361 @Temperature 200 °C |
0.361 @Temperature 392 °F |
Condition T6 | |
| 0.364 @Temperature 250 °C |
0.364 @Temperature 482 °F |
Condition T6 | |
| 0.369 @Temperature 300 °C |
0.369 @Temperature 572 °F |
Condition T6 | |
| Shear Modulus | 23.0 GPa @Temperature 300 °C |
3340 ksi @Temperature 572 °F |
Condition T6 |
| 24.0 GPa @Temperature 200 °C |
3480 ksi @Temperature 392 °F |
Condition T6 | |
| 24.0 GPa @Temperature 250 °C |
3480 ksi @Temperature 482 °F |
Condition T6 | |
| 25.0 GPa @Temperature 150 °C |
3630 ksi @Temperature 302 °F |
Condition T6 | |
| 26.0 GPa @Temperature 100 °C |
3770 ksi @Temperature 212 °F |
Condition T6 | |
| 28.0 GPa @Temperature 20.0 °C |
4060 ksi @Temperature 68.0 °F |
Condition T6 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.9 - 23.9 µm/m-°C @Temperature 20.0 - 100 °C |
12.7 - 13.3 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 23.7 - 24.7 µm/m-°C @Temperature 20.0 - 200 °C |
13.2 - 13.7 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 24.5 - 25.5 µm/m-°C @Temperature 20.0 - 300 °C |
13.6 - 14.2 µin/in-°F @Temperature 68.0 - 572 °F |
||
| Thermal Conductivity | 121.9 W/m-K @Temperature 30.0 °C |
846.0 BTU-in/hr-ft²-°F @Temperature 86.0 °F |
|
| 130.9 W/m-K @Temperature 100 °C |
908.4 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| 144.6 W/m-K @Temperature 200 °C |
1004 BTU-in/hr-ft²-°F @Temperature 392 °F |
||
| 155.7 W/m-K @Temperature 300 °C |
1081 BTU-in/hr-ft²-°F @Temperature 572 °F |
||
| 156.1 W/m-K @Temperature 400 °C |
1083 BTU-in/hr-ft²-°F @Temperature 752 °F |
||
| Melting Point | 512 - 659 °C | 954 - 1220 °F | |
| Solidus | 512.3 - 518.3 °C | 954.1 - 964.9 °F | |
| Liquidus | 653.6 - 659.3 °C | 1208 - 1219 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 94 % | 94 % | As Balance |
| Copper, Cu | 5.0 % | 5.0 % | |
| Titanium, Ti | 1.0 % | 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000570 - 0.00000610 ohm-cm | 0.00000570 - 0.00000610 ohm-cm |