PEAK Werkstoff DISPAL S225 Aluminum Alloy, AlSi35Fe2Ni, Condition F

Category Metal , Nonferrous Metal , Aluminum Alloy
Manufacturer PEAK Werkstoff
Trade Name DISPAL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PEAK Werkstoff DISPAL S225 Aluminum Alloy, AlSi35Fe2Ni, Condition F.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Information provided by PEAK Werkstoff GmbH
Physical Properties Metric English Comments
Density 2.451 - 2.709 g/cc
0.08855 - 0.09787 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers 85
85
Tensile Strength at Break >= 97.0 MPa

@Temperature 300 °C
 >= 14100 psi

@Temperature 572 °F
>= 116 MPa

@Temperature 250 °C
 >= 16800 psi

@Temperature 482 °F
>= 154 MPa

@Temperature 200 °C
 >= 22300 psi

@Temperature 392 °F
>= 180 MPa

@Temperature 150 °C
 >= 26100 psi

@Temperature 302 °F
>= 218 MPa

@Temperature 20.0 °C
 >= 31600 psi

@Temperature 68.0 °F
Tensile Strength, Yield >= 60.0 MPa

@Temperature 300 °C
 >= 8700 psi

@Temperature 572 °F
>= 71.0 MPa

@Temperature 250 °C
 >= 10300 psi

@Temperature 482 °F
>= 86.0 MPa

@Temperature 200 °C
 >= 12500 psi

@Temperature 392 °F
>= 105 MPa

@Temperature 150 °C
 >= 15200 psi

@Temperature 302 °F
>= 128 MPa

@Temperature 20.0 °C
 >= 18600 psi

@Temperature 68.0 °F
Elongation at Break >= 1.0 %

@Temperature 20.0 °C
 >= 1.0 %

@Temperature 68.0 °F
>= 1.9 %

@Temperature 150 °C
 >= 1.9 %

@Temperature 302 °F
>= 2.0 %

@Temperature 200 °C
 >= 2.0 %

@Temperature 392 °F
>= 3.2 %

@Temperature 250 °C
 >= 3.2 %

@Temperature 482 °F
>= 5.9 %

@Temperature 300 °C
 >= 5.9 %

@Temperature 572 °F
Modulus of Elasticity >= 64.0 GPa

@Temperature 300 °C
 >= 9280 ksi

@Temperature 572 °F
>= 65.0 GPa

@Temperature 250 °C
 >= 9430 ksi

@Temperature 482 °F
>= 66.0 GPa

@Temperature 200 °C
 >= 9570 ksi

@Temperature 392 °F
>= 77.0 GPa

@Temperature 150 °C
 >= 11200 ksi

@Temperature 302 °F
>= 86.0 GPa

@Temperature 20.0 °C
 >= 12500 ksi

@Temperature 68.0 °F
Poissons Ratio 0.264

@Temperature 20.0 °C
 0.264

@Temperature 68.0 °F
0.267

@Temperature 100 °C
 0.267

@Temperature 212 °F
0.268

@Temperature 150 °C
 0.268

@Temperature 302 °F
0.269

@Temperature 200 °C
 0.269

@Temperature 392 °F
0.27

@Temperature 250 °C
 0.27

@Temperature 482 °F
0.274

@Temperature 300 °C
 0.274

@Temperature 572 °F
Shear Modulus 34.0 GPa

@Temperature 300 °C
 4930 ksi

@Temperature 572 °F
36.0 GPa

@Temperature 250 °C
 5220 ksi

@Temperature 482 °F
37.0 GPa

@Temperature 150 °C
 5370 ksi

@Temperature 302 °F
37.0 GPa

@Temperature 200 °C
 5370 ksi

@Temperature 392 °F
38.0 GPa

@Temperature 100 °C
 5510 ksi

@Temperature 212 °F
39.0 GPa

@Temperature 20.0 °C
 5660 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 14.6 - 15.6 µm/m-°C

@Temperature 20.0 - 100 °C
 8.11 - 8.67 µin/in-°F

@Temperature 68.0 - 212 °F
15.5 - 16.5 µm/m-°C

@Temperature 20.0 - 200 °C
 8.61 - 9.17 µin/in-°F

@Temperature 68.0 - 392 °F
16.5 - 17.5 µm/m-°C

@Temperature 20.0 - 300 °C
 9.17 - 9.72 µin/in-°F

@Temperature 68.0 - 572 °F
Thermal Conductivity 103.7 W/m-K

@Temperature 400 °C
 719.7 BTU-in/hr-ft²-°F

@Temperature 752 °F
110.4 W/m-K

@Temperature 300 °C
 766.2 BTU-in/hr-ft²-°F

@Temperature 572 °F
115 W/m-K

@Temperature 200 °C
 798 BTU-in/hr-ft²-°F

@Temperature 392 °F
120 W/m-K

@Temperature 100 °C
 833 BTU-in/hr-ft²-°F

@Temperature 212 °F
126.6 W/m-K

@Temperature 30.0 °C
 878.6 BTU-in/hr-ft²-°F

@Temperature 86.0 °F
Melting Point 567 - 903 °C
1050 - 1660 °F
Solidus 567.2 - 573.2 °C
1053 - 1064 °F
Liquidus 897 - 903 °C
1650 - 1660 °F
Component Elements Properties Metric English Comments
Aluminum, Al 62 %
62 %
As Balance
Iron, Fe 2.0 %
2.0 %
Nickel, Ni 1.0 %
1.0 %
Silicon, Si 35 %
35 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000810 - 0.00000880 ohm-cm
0.00000810 - 0.00000880 ohm-cm