Oxford Polymers Polysulfone PSF P170-64170 White PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer Oxford Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Oxford Polymers Polysulfone PSF P170-64170 White PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Polysulfone injection molding grade, precolored white Processing and Delivery Form: Pellets and Injection Molding Special Characteristics: Continuous use up to 300(f)Information provided by Oxford Polymers
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption at Saturation 0.300 %
0.300 %
ASTM D570
Linear Mold Shrinkage, Flow 0.00700 cm/cm

@Thickness 3.17 mm
0.00700 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.29 MPa
10050 psi
ASTM D638
Elongation at Break 50.0 - 100 %
50.0 - 100 %
ASTM D638
Flexural Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 2.83 GPa
410 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 174 °C
345 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 321 - 343 °C
610 - 650 °F
Middle Barrel Temperature 329 - 354 °C
625 - 670 °F
Front Barrel Temperature 335 - 360 °C
635 - 680 °F
Nozzle Temperature 335 - 360 °C
635 - 680 °F
Melt Temperature 332 - 349 °C
630 - 660 °F
Mold Temperature 104 - 138 °C
220 - 280 °F
Drying Temperature 132 °C
270 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour